Microstructure Modification and Oxygen Mobility of CeZrO2 Nanocrystal Doped With Y and Fe Metals.

CeZrO2-nanocrystals doped with Y3+ and Fe2+ have been successfully synthesized using the microemulsion method. In this study, the synergetic effect of the synthesis parameters on the formation of structure and catalytic property were reported. XRD analysis found that both doped samples reveal the symmetrical cubic phase and mix in a homogeneous solid solution. The crystallite size of both samples was in nanoscale, which were 11 and 15 nm for CZF and CZY, respectively. This finding was consistent with the physical size investigated by TEM, which was approximately 10 nm for both samples. Meanwhile, isotherm profiles for both samples appeared as the type IV group in the IUPAC classification which was the mesoporous materials. CZY crystal had higher BET surface area than CZF crystal, which was 141.30 and 135.5 m2/g, respectively. Oxygen mobility study found that CZF crystal promotes to active at lower temperature, which is 274.2°C, than CZY at 302.7°C. CZF crystal also revealed the higher oxygen removal, which was 286.35 mmol/g, than CZY was 250.49 mmol/g. The doping of transition metal, Fe into CeZrO2 tended to reduce the oxygen mobility's activation temperature, while the addition of rare earth metal, Y into CeZrO2 leaded to remarkable increase of surface area. [ABSTRACT FROM AUTHOR]
Copyright of AIP Conference Proceedings is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)