Thermal-Induced Phase Transformation Behavior of NiTiNb Hypoeutectic, Eutectic, and Hypereutectic Alloys.

Tytuł :
Thermal-Induced Phase Transformation Behavior of NiTiNb Hypoeutectic, Eutectic, and Hypereutectic Alloys.
Autorzy :
Yin, Huilin
Ma, Guohua
Fan, Qichao
Wang, Yingying
Huang, Shuke
Yi, Yong
Pokaż więcej
Temat :
HYPEREUTECTIC alloys
Źródło :
Metals (2075-4701); Feb2019, Vol. 9 Issue 2, p214, 1p
Czasopismo naukowe
In the present work, three NiTiNb alloys with nominal compositions of Ni50–x/2Ti50–x/2Nbx (x = 18, 20 and 22, at.%) were prepared. The microstructure, thermal-induced phase transformation, and phase components of NiTiNb hypoeutectic, eutectic, and hypereutectic alloys were investigated by scanning electron microscopy coupled with energy dispersive spectrometer (SEM/EDS), differential scanning calorimetry (DSC), and X-ray diffraction (XRD), respectively. Two peaks occurred in the DSC curves of Ni41Ti41Nb18 solution at 750 and 850 °C. The different microstructures of NiTiNb hypoeutectic, eutectic and hypereutectic alloys, the occurrence of two peaks in the DSC curves, and the characteristic of martensite transformation temperature were analyzed and discussed. The results show that different Nb content leads to different microstructures of Ni50–x/2Ti50–x/2-Nbx alloys. Moreover, the difference of Ni/Ti ratio between the primary NiTi matrix and NiTi in eutectic structure strongly influenced the phase transformation behavior that the DSC curves of Ni41Ti41Nb18 alloy show two peaks. Furthermore, under the same solution treatment, the Ni40Ti40Nb20 alloy has a lower Ms than the other two alloys. The Ms has a tendency to decrease with an increase in solution temperature. [ABSTRACT FROM AUTHOR]
Copyright of Metals (2075-4701) is the property of MDPI Publishing and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies