Effect of surface treatments on the localized corrosion resistance of the AA2198‐T8 aluminum lithium alloy welded by FSW process.

In this work, the effect of eight types of surface treatments on the corrosion resistance of friction stir welded samples of an AA2198‐T8 Al‐Cu‐Li alloy were tested and compared in an attempt to find suitable alternatives to toxic and carcinogenic hexavalent chromium treatments. All the samples were anodized and subjected to different post‐anodizing treatments. The post‐anodizing treatments were (1) hydrothermal treatment in Ce (NO3)3 6H2O solution; (2) hydrothermal treatment in Ce (NO3)3 6H2O solution with H2O2; (3) hydrothermal treatment in boiling water; (4) hexavalent chromium conversion coating; and (5) immersion in BTSE (bis‐1,2‐(triethoxysilyl) ethane. The corrosion resistance of the treated samples was evaluated by immersion tests in sodium chloride solution (0.1 mol L−1 NaCl) and electrochemical impedance spectroscopy (EIS) of the friction stir weldment. The results showed that among the alternative treatments, the Ce‐containing solutions presented the best corrosion resistance, especially when used without peroxide. [ABSTRACT FROM AUTHOR]
Copyright of Surface & Interface Analysis: SIA is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)