Structure of HfO2 modified with Y, Gd, and Zr at ambient conditions and high pressures.

High-resolution and high-pressure X-ray diffraction measurements were performed to determine the effects of 5% Y, 3% Gd, and 50% Zr substitution on the crystal structure and polymorphism of HfO2. High-resolution experiments at ambient pressure show a mixture of monoclinic and cubic fluorite phases in 5% Y:HfO2 and 3% Gd:HfO2, while 50% Zr:HfO2 formed a monoclinic, single-phase solid solution. Crystallographic refinement using the Rietveld method indicates that Y and Gd substitute for Hf in both the monoclinic and cubic phases. High-pressure X-ray diffraction was performed in situ up to 31 GPa and shows that the pressure-induced phase transitions were reduced with the addition of either Y, Gd, or Zr relative to the transition pressures in undoped HfO2. The pressure-induced changes in lattice parameter, relative volume, and spontaneous strain are reported. [ABSTRACT FROM AUTHOR]
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)