Structural parameters, elastic constants, and their related properties of MgCa with a cubic CsCl‐type structure under high pressure up to 16 GPa are investigated using the pseudopotential plane‐wave approach in the framework of the density functional theory as implemented in the CASTEP code. The results indicate that MgCa possesses a brittle nature below 1.4 GPa and begins to be prone to ductility when the pressure goes beyond this value. The tetragonal shear parameter is found to vanish at around 7 GPa. The analyses of the anisotropy factors show that MgCa is highly anisotropic. The magnitude of the anisotropy increases monotonically with applied pressure. The single crystal azimuthal anisotropy for longitudinal and transverse waves is determined. The variation of the longitudinal and shear‐wave velocities with the direction of propagation is estimated at 0 and 16 GPa pressure. The Cauchy condition is found to be strongly violated, reflecting the important contribution from the noncentral many‐body forces in the crystal. In addition, the specific heat capacity CV and the entropy S at elevated temperatures up to 600 K are studied. At zero‐pressure and T = 300 K, our calculation yields values of CV ≈ 47.31 J mol−1 K−1 and S ≈ 66.06 J mol−1 K−1. [ABSTRACT FROM AUTHOR]
Copyright of Physica Status Solidi (B) is the property of Wiley-Blackwell and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)