The microstructure just below the fracture surface in hydrogen-charged stable austenitic SUS 316L stainless steel, which was subjected to a low strain rate tensile test at −70°C, was studied by a combination of the focused-ion-beam method and transmission electron microscopy. An amorphous region with a chemical composition almost identical to that of the polycrystalline region was found under the lath-like structure on the fracture surface, although no deterioration of tensile properties by hydrogen appeared. In the amorphous region, band-like regions with wavy contrasts were observed, which were often accompanied by cracks at the boundaries. The presence of the amorphous region with band-like regions implies that amorphization occurred due to high-density vacancies accompanied by agglomerations of excess vacancies in the hydrogen-charged SUS 316L stainless steel that was tensile-tested at low temperatures. [ABSTRACT FROM AUTHOR]
Copyright of Philosophical Magazine Letters is the property of Taylor & Francis Ltd and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Zaloguj się, aby uzyskać dostęp do pełnego tekstu.