Passivation of the n-InP(100) surface with sodium sulfide (Na2S) aqueous solution is analyzed by photoluminescence (PL) and X-ray photoelectron spectroscopy (XPS). The room-temperature PL intensity increases essentially even after short treatment with sulfide solution for 1 min. The enhancement in the room-temperature PL intensity after passivation decreases with the increase in the bulk doping level of the semiconductor. Time-resolved PL studies performed at liquid-nitrogen temperature indicate reduction in the surface recombination velocity. This improvement of the PL intensity occurs just after transformation of the native oxide layer consisting mainly of indium phosphates to the passivating layer consisting of indium sulfides and oxides. The surface bands in n-InP(100) remained nearly flat both before and after sulfide passivation. [ABSTRACT FROM AUTHOR]
Copyright of Semiconductors is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Zaloguj się, aby uzyskać dostęp do pełnego tekstu.