Chemical composition optimization and characterization of the NiO/B2O3-Al2O3 system as a catalyst for ethylene oligomerization.

The samples of the NiO/B2O3-Al2O3 system with NiO contents from 0.48 to 38.30 wt % were synthesized by the impregnation of borate-containing alumina (20 wt % B2O3). It was found that nickel oxide occurred in an X-ray amorphous state in the samples containing to 23.20 wt % NiO. At a NiO content of 4.86 wt % or higher, the support was blocked by the modifier to cause a decrease in the specific surface area from 234 to 176 m2/g and in the amount of acid sites from 409–424 to 333 μmol/g. An extremal character of the dependence of catalyst activity in ethylene oligomerization on NiO content was found with a maximum in the range of 4.86–9.31 wt %. Based on spectroscopic data, it was found that ethylene activation on the NiO/B2O3-Al2O3 catalyst can be associated with the presence of Ni2+ cations, which chemically interact with the support. The catalyst containing 4.86 wt % NiO at 200°C, a pressure of 4 MPa, and an ethylene supply rate of 1.1 h−1 provided almost complete ethylene conversion at the yield of liquid oligomerization products to 90.0 wt %; the total concentration of C8+ alkenes in these products was 89.0 wt %. [ABSTRACT FROM AUTHOR]
Copyright of Kinetics & Catalysis is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)