One-step hydrothermal synthesis and characterization of LiNi 0.5 Mn 0.5 O 2 nanoparticles.

Tytuł :
One-step hydrothermal synthesis and characterization of LiNi 0.5 Mn 0.5 O 2 nanoparticles.
Autorzy :
Wu, Tian
Wan, Yunhai
Huang, Qing
Xia, Hui
Pokaż więcej
Temat :
LITHIUM compounds
CHEMICAL synthesis
HYDROTHERMAL synthesis
LITHIUM-ion batteries
NANOPARTICLE synthesis
X-ray absorption
CYCLIC voltammetry
Źródło :
Materials Technology; Jun2015, Vol. 30 Issue A4, pA176-A180, 1p
Czasopismo naukowe
Facile preparation of electrode materials possesses prime importance to commercialize new energy storage materials. Herein, a facile one-step hydrothermal method is used to prepare the LiNi0.5Mn0.5O2nanoparticles as a cathode material for lithium-ion batteries (LIBs). The physicochemical and electrochemical properties of LiNi0.5Mn0.5O2nanoparticles were characterized by scanning electron microscopy, X-ray diffraction, transmission electron microscopy, X-ray absorption spectroscopy, charge–discharge tests and cyclic voltammetric measurements. The product shows pure crystalline phase of LiNi0.5Mn0.5O2, while the nanostructure is comprised of macrospores ranging from 10 to 50 nm. It delivers an initial discharge capacity of 137.5 mAh g−1between 2.5 and 4.3 V at a 0.1 °C rate. It is shown that the reported facile preparation is applicable to scale-up applications of layered cathodes for LIBs. [ABSTRACT FROM AUTHOR]
Copyright of Materials Technology is the property of Taylor & Francis Ltd and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies