Protective film formation on AA2024-T3 aluminium alloy by leaching of lithium carbonate from an organic coating

Tytuł :
Protective film formation on AA2024-T3 aluminium alloy by leaching of lithium carbonate from an organic coating
Autorzy :
Yanwen Liu, Peter Visser, Xiaorong Zhou, Stuart B. Lyon, Teruo Hashimoto, Michele Curioni, Ali Gholinia, George E. Thompson, Gerard Smyth, Simon R. Gibbon, Derek Graham, Johannes M. C. Mol, and Herman Terryn
Pokaż więcej
Temat :
equipment and supplies
AA2024 aluminium alloy
corrosion
inhibition
leaching
technology, industry, and agriculture
lithium carbonate
Źródło :
Liu, Y, Visser, P, Zhou, X, Lyon, S B, Hashimoto, T, Curioni, M, Gholinia, A, Thompson, G E, Smyth, G, Gibbon, S R, Graham, D, Mol, J MC & Terryn, H 2015, ' Protective film formation on AA2024-T3 aluminium alloy by leaching of lithium carbonate from an organic coating ', Electrochemical Society. Journal, vol. 163, no. 3, pp. 45-53 . https://doi.org/10.1149/2.0021603jes
Journal of the Electrochemical Society, 163 (3), 2016
Wydawca :
Electrochemical Society, 2015.
Rok publikacji :
2015
Kolekcja :
Manchester_eScholar_Services_enriched
NARCIS
NARCIS_enriched
Manchester_eScholar_Services
Opis pliku :
text; application/pdf; application/octet-stream
Język :
English
ISSN :
0013-4651
DOI :
10.1149/2.0021603jes
Numer akcesji :
edsair.dedup.wf.001..a1294ab3ea9acf642b83d74ed1063869
An investigation into corrosion inhibition properties of a primer coating containing lithium carbonate as corrosion inhibitive pigment for AA2024 aluminum alloy was conducted. It was found that, during neutral salt spray exposure, a protective film of about 0.2 to 1.5 μm thickness formed within the area where an artificial defect was introduced by scribing through the coating to the base alloy. This film showed a multilayered structure consisting of a relatively compact layer near the alloy substrate, a porous middle layer and a columnar outer layer. The thicknesses of the layers varied, as a consequence of the difference in the local concentration of lithium species leaching from the primer coating. The presence of the film in the scribed area significantly reduced corrosion of the alloy, with little consumption of the metal substrate within the scribed area during neutral salt spray exposure. Furthermore, the presence of the protective film resulted in a significant increase of impedance modulus, measured after the salt spray exposure.

Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies