Jet Milling as an Alternative Processing Technique for Preparing Polysulfone Hard Nanocomposites

Tytuł :
Jet Milling as an Alternative Processing Technique for Preparing Polysulfone Hard Nanocomposites
Autorzy :
Amaia Llorente
Berna Serrano
Juan Baselga
Gabriel Gedler
Rahmi Ozisik
Pokaż więcej
Temat :
Materials of engineering and construction. Mechanics of materials
TA401-492
Źródło :
Advances in Materials Science and Engineering, Vol 2019 (2019)
Wydawca :
Hindawi Limited, 2019.
Rok publikacji :
2019
Kolekcja :
LCC:Materials of engineering and construction. Mechanics of materials
Typ dokumentu :
article
Opis pliku :
electronic resource
Język :
English
ISSN :
1687-8434
1687-8442
Relacje :
https://doaj.org/toc/1687-8434; https://doaj.org/toc/1687-8442
DOI :
10.1155/2019/3501402
Dostęp URL :
https://doaj.org/article/34c5f4174faf4c9a869097495ae1027b
Numer akcesji :
edsdoj.34c5f4174faf4c9a869097495ae1027b
Czasopismo naukowe
This work describes how a solid-state blending method such as jet milling can be used to successfully prepare polysulfone (PSU)/γ-alumina nanocomposites. For comparison purposes, conventional melt extrusion was used as well. Morphological analysis revealed how jet mill blending allows obtaining well-dispersed γ-alumina nanoparticles within a polysulfone matrix without any surface treatment, with an important decrease of particle size promoted by the breakup of agglomerates and aggregates due to the particle-particle impacts during processing, which was not observed in the extruded nanocomposites. DSC analysis demonstrated that jet-milling processing promoted Tg enhancements with alumina addition, while TGA experiments confirmed the increment of thermal stability of the nanocomposites prepared by jet milling when compared with the composites prepared by extrusion. The tensile tests showed that ductility remains at a high value for milled nanocomposites, which agreed with the fracture surface images revealing large plastic deformation as a function of the alumina content. This comparative study indicates that the dispersion of nanoparticles in PSU was more homogeneous, with smaller nanoparticles when preparing nanocomposites using jet milling, showing a strong correlation with the enhanced final properties of the nanocomposites.
Zaloguj się, aby uzyskać dostęp do pełnego tekstu.

Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies