A new mineral species, zhanghuifenite, ideally Na3Mn42+ Mg2Al(PO4)6, has been found in the Santa Ana mine, San Luis province, Argentina. It occurs in irregular veinlets or patches, 5 mm thick, in a nodule of beusite interlaminated with lithiophilite. Broken pieces of zhanghuifenite are blocky or tabular. Single crystals are up to 0.8 x 0.5 x 0.5 mm. No twinning or parting is observed macroscopically. The mineral is deep green, transparent with pale green streak and vitreous luster. It is brittle and has a Mohs hardness of ~5 with good cleavage on {010}. The measured and calculated densities are 3.63(2) and 3.62 g/cm³, respectively. Optically, zhanghuifenite is biaxial (+), with α = 1.675(2), β = 1.680(2), γ = 1.690(2) (white light), 2V (meas) = 74(2)°, and 2V (calc) = 71°. The calculated compatibility index based on the empirical formula is 0.020 (excellent). An electron microprobe analysis yields an empirical formula (based on 24 O apfu) (Na2.80Ca0.11)Σ2.91 (Mn3.092+Fe0.472+ Mg0.36)Σ3.92(Mg1.31 Fe0.692+)Σ2.00 (Al0.81Fe0.193+) (PO4)6. Zhanghuifenite is insoluble in water or hydrochloric acid. Zhanghuifenite is isostructural with bobfergusonite, a member of the alluaudite supergroup. It is monoclinic, with space group P21/n, Z = 4, and unit-cell parameters a = 12.8926(3), b = 12.4658(3), c = 10.9178(2) Å, β = 97.9200(10)°, and V = 1737.93(7) ų. The crystal structure of zhanghuifenite contains six octahedral M (= Mn, Fe, Mg, Al) sites and five X (= Na, Mn, Ca) sites with coordination numbers between 6 and 8. The six M octahedra share edges to form two types of kinked chains extending along [101], with one consisting of M1-M4-M5 and the other M2-M3-M6. These chains are joined by PO4 tetrahedra to form sheets parallel to (010), which are linked together through corner-sharing between PO4 tetrahedra and MO6 octahedra in the adjacent sheets, leaving open channels parallel to a, where the large X cations are situated. Zhanghuifenite differs from bobfergusonite in two major aspects. One is that the M4 and M5 sites in the former are mainly occupied by Mg, but by Fe2+ and Fe3+, respectively, in the latter. The other is that the X2-X5 sites in zhanghuifenite are all nearly or fully filled with Na, resulting in 3 Na apfu in the ideal formula, but X4 and X5 are merely half-occupied in bobfergusonite, giving rise to 2 Na apfu. [ABSTRACT FROM AUTHOR]
Copyright of American Mineralogist is the property of De Gruyter and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)